Bryansk, Bryansk, Russian Federation
Babbit 83 crack resistance test in accordance with SSR 25-506-85 was carried out. By finite element method there were defined values of stress intensity factors in flat samples with a grown crack. The fracture viscosity characteristics of babbit are obtained. On the basis of a macro-fractographic analysis of wear fractures of a babbit sample and a finite element procedure for the definition of values of stress intensity factors the cha-racteristics of cyclic crack resistance are obtained. It is shown that a final fracture is realized at 3 МПа , and a transition from an elastic stage to the stage elastoplastic development of a crack is realized at 2,0…2,8 МПа .
babbit B83, static loading, cyclic loading, disintegration characteristics, finite element method, stress intensity factor, invariant J-integral, cyclic crack resistance
1. Kuzmenko, А.G. Procedure for assessment of fatigue resistance of antifriction materials for slider bearings / А.G. Kuzmenko, А.V. Yakovlev, М.V. Zernin // Factory Laboratory. - 1984. - № 8. - pp. 77-79.
2. Zernin, М.V. To investigation of fatigue life of babbit layer in heavy-loaded slider bearings / М.V.Zernin, А.V.Yakovlev// Factory Laboratory. - 1997. - № 11. - pp. 39-47.
3. Zernin, М.V. Experimental investigations of crack system origin in babbit layers applied on steel base / М.V.Zernin, А.G.Kuzmenko, P.N.Savonichev // Factory Laboratory. - 1998. - Vol. 64. - № 1. - pp. 38-44.
4. Zernin, М.V. Experimental assessment of asymme-try impact of loading cycle upon fatigue life of babbit layers /М.V.Zernin // Factory Laboratory. - 1998. - Vol. 64. - № 4. - pp. 48-52.
5. Zernin, М.V. Contact creep of babbit layer in slider bearings / М.V.Zernin, А.G.Kuzmenko, А.V.Yakovlev // Factory Laboratory. - 2008. - Vol. 74. - № 5. - pp. 58-62.
6. Morozov, Е.М. Contact Problems of Destruction Mechanics / Е.М. Morozov, М.V. Zernin. - 2-d ed. - М.: Librocom, 2010. - pp. 544.
7. Zernin, М.V. Criteria of stressed state equivalence and generalized diagram of tinbased babbit deformation /М.V.Zernin// Bulletin of Bryansk State Technical University. - 2014. - №3. - pp. 26-34.
8. Broek, D. Fundamentals of Destruction Mechanics /D.Broek. - М.: Higher School, 1980. - pp. 368.
9. Cherepanov, G.P. Mechanics of Brittle Fracture / G.P.Cherepanov. - М.: Science, 1974. - pp. 640.
10. Morozov, Е.М. ANSYS in Engineer’s Hands /Е.М.Morozov. - М.: Lenand, 2010. - pp. 456.
11. SSR 25.506-85. Computations and Strength Tests. Methods of Metal Mechanical Tests. Definition of Crack Resistance Characteristics (fracture tough-ness) at Static Loading.
12. Murakamy, Yu. Reference Book on Stress Intensity Factors /Yu.Murakamy. - М.: Мир, 1990. - pp. 566.