The optimal composition of adhesive compositions was found which based on urea-formaldehyde resins for the manufacture of low-toxic plywood with improved strength. The modes of activation fillers adhesives with using of different electromagnetic fields was established, to ensure the maximum reduction in the emission of free formaldehyde (27% below the level of toxicity E1 - microwave EMF) from finished plywood and an increase in its strength characteristics (2.2 times - EMF microwave). The results obtained reduce consumer´s risks to a level of 0.67 (EMF microwave) and 0.75 (SIMP) from the standard value of 1 and provide a significant economic benefit of reducing the cost of manufacture of plywood and emissions of formaldehyde in the atmosphere.
Plywood, nanomaterials, clinoptilolite, synthetic silica, Aerosil formaldehyde, weak pulsed magnetic fields, electromagnetic field of ultrahigh frequency, filler, urea-formaldehyde resin, a toxicity issue, the tensile strength of plywood at shearing, the internal stress of the adhesive composition.
СЕКЦИЯ 1: СОВРЕМЕННЫЕ МАТЕРИАЛЫ, ПОКРЫТИЯ
И ТЕХНОЛОГИИ ИХ СОЗДАНИЯ
УДК 674.8: 574
Технология получения экологичной и прочной фанеры с использованием электромагнитных полей
CREATING THE TECHNOLOGY OF ENVIRONMENTALLY FRIENDLY AND DURABLE PLYWOOD WITH USING ELECTROMAGNETIC FIELDS
Анисимов М.В.
ФГБОУ ВПО «Воронежская государственная лесотехническая академия»
г. Воронеж, Россия
DOI: 10.12737/6094
Аннотация: Определены оптимальные рецептуры клеевых композиций на основе карбамидоформальдегидных смол для изготовления малотоксичной фанеры повышенной прочности. Установлены режимы активации наполнителей клеев различными электромагнитными полями, обеспечивающие максимальное снижение эмиссии свободного формальдегида (на 27% ниже уровня токсичности Е1 – ЭМП СВЧ) из готовой фанеры и увеличение ее прочностных характеристик (в 2,2 раза – ЭМП СВЧ). Полученные результаты уменьшают потребительские риски до уровня 0,67 (ЭМП СВЧ) и 0,75 (СИМП) от стандартного значения 1 и обеспечивают существенный экономический эффект от снижения себестоимости изготовления фанеры и сокращения вредных выбросов формальдегида в атмосферу.
Summary: The optimal composition of adhesive compositions was found which based on urea-formaldehyde resins for the manufacture of low-toxic plywood with improved strength. The modes of activation fillers adhesives with using of different electromagnetic fields was established, to ensure the maximum reduction in the emission of free formaldehyde (27% below the level of toxicity E1 - microwave EMF) from finished plywood and an increase in its strength characteristics (2.2 times - EMF microwave). The results obtained reduce consumer's risks to a level of 0.67 (EMF microwave) and 0.75 (SIMP) from the standard value of 1 and provide a significant economic benefit of reducing the cost of manufacture of plywood and emissions of formaldehyde in the atmosphere.
Ключевые слова: фанера, наноматериалы, клиноптилолит, искусственный кремнезем, аэросил формальдегид, слабые импульсные магнитные поля, электромагнитное поле сверхвысокой частоты, наполнитель, карбамидоформальдегидная смола, токсичность, эмиссия, предел прочности фанеры при скалывании, внутренние напряжения клеевой композиции.
Keywords: Plywood, nanomaterials, clinoptilolite, synthetic silica, Aerosil formaldehyde, weak pulsed magnetic fields, electromagnetic field of ultrahigh frequency, filler, urea-formaldehyde resin, a toxicity issue, the tensile strength of plywood at shearing, the internal stress of the adhesive composition.
Область исследований, характеристика проблемы.
В России и за рубежом существует проблема экологического ограничения использования фанеры в помещениях различного типа, регламентируемая необходимым уровнем эмиссии формальдегида.