This paper presents the results of a study of the corrosion resistance of building structures OF NLMK's CCPP and CDP. It was found that the average percentage of damage is 8.69%, and the areas with high humidity and gas emissions have the greatest corrosion wear of elements. Using a mathematical model of corrosion for zinc and steel, their expected corrosion losses are calculated. It is shown that the greatest mass loss is observed in areas with a concentration of hydrogen chloride above the background value. The results of accelerated corrosion tests of a zinc coating with a crystallite size from 0.6 to 3.5 microns showed that reducing the crystallite size to 0.6 microns reduces the corrosion rate by 2 times, which should increase the service life of the structure by 1.5-2 times compared to traditional materials.
corrosion resistance, assessment of the technical condition of building structures, Zn-coating
1. Mihaylovskiy Yu.N., Sokolov N.A. Novye predstavleniya o mehanizme stimuliruyuschego deystviya sernistogo gaza na atmosfernuyu korroziyu metallov // Zaschita metallov. 1985. T. 21. №2. S. 214-220.
2. Strekalov P.V., Do Than' B. Modelirovanie atmosfernoy korrozii uglerodistoy stali vo vlazhnyh tropikah po rezul'tatam trehmesyachnyh i godovyh ispytaniy // Zaschita metallov. - 2005. - T. 41. - №3. - S. 302-315.
3. Karpov V.A., Lapiga A.G., Kalinina E.V., Mihaylova O.L., Koval'chuk Yu.L. Modelirovanie atmosfernoy korrozii v tropicheskom klimate V'etnama / V.A. Karpov, i dr. // Korroziya: materialy, zaschita. - 2016. - № 8. - S. 1-10.
4. Gataullin I.N. Eksperimental'nye issledovaniya korrozionnogo iznosa metallicheskih konstrukciy v agressivnyh sredah// Izvestiya KGASA, 2003, №1. - S.42-47.
5. Mihaylov V.V., Kolobanov A.S., Lifincev O.I., Lifincev A.I. Issledovanie korrozionnoy stoykosti konstrukciy pokrytiya cehov holodnogo prokata stali // Vestnik Volgogradskogo gosudarstvennogo arhitekturno-stroitel'nogo universiteta. Seriya: Stroitel'stvo i arhitektura. 2007. № 7. S. 28-32.
6. Kolobanov A.S., Tret'yakova S.V., Sabitov L.S. Obsledovanie zdaniy i sooruzheniy, rabotayuschih v usloviyah agressivnyh gazovozdushnyh sred // Izvestiya Kazanskogo gosudarstvennogo arhitekturno-stroitel'nogo universiteta. 2010. № 1 (13). S. 106-110.
7. Ulybin A.V., Zubkov S.V., Fedotov S.D., Kukushkina G.A., Chernenko E.V. Tehnicheskoe obsledovanie stroitel'nyh konstrukciy kompleksa proizvodstvennyh zdaniy // Stroitel'stvo unikal'nyh zdaniy i sooruzheniy. 2014. № 7 (22). S. 194-217.
8. Fedotov S.D., Ulybin A.V., Shabrov N.N. O metodike opredeleniya korrozionnogo iznosa stal'nyh konstrukciy. // Inzhenerno-stroitel'nyy zhurnal. 2013. № 1 (36). S. 12-20.
9. Proskurkin E.V., Gelovani V.A., Sonk A.N., Petrov I.V., Yarema I.P., Suhomlin D.A. Cinkovye pokrytiya - osnovnye sovremennye sistemy zaschity trub ot korrozii // Stal'. 2018. № 6. S. 32-37.
10. Kablov E.N., Nikiforov A.A., Demin S.A., Chesnokov D.V., Vinogradov S.S. Perspektivnye pokrytiya dlya zaschity ot korrozii uglerodistyh staley // Stal'. 2016. № 6. S. 70-81.
11. Celuykin V.N., Koreshkova A.A. O korrozionnyh svoystvah kompozicionnyh pokrytiy cink-uglerodnye nanotrubki // Korroziya: materialy, zaschita. 2014. №3. S. 31-34.
12. Lahotkin Yu.V., Dushik V.V., Kuz'min V.P., Rozhanskiy N.V. Nanostrukturirovannye tverdye pokrytiya - klyuch k bezopasnosti ekspluatacii oborudovaniya v ekstremal'nyh usloviyah // Korroziya: materialy, zaschita. 2014. № 3. S. 21-26.