for anybody not a secret that wood — is material which is actively applied in construction, after all it possesses excellent operational characteristics, and along with that has really beautiful appearance. Nevertheless, and it has one feature: when processing wood the large number of waste and scraps, especially is formed in case the product has a difficult form or big dimensions. For the last several tens years the question of more effective use of this material was actual. In many respects it influenced development of production of plywood, and then and wood plates. But the XXI century became an era of composite materials: it is possible to tell with confidence that with the advent of DPK there was the next industrial revolution. Any material is characterized by some parameters. One of the main characteristics of DPK is strength at compression. The technique and results of test wood polymer - a sand composite on compression is given in article.
wood, composite materials, compression tests
УДК 674.8:620.22
ИСПЫТАНИЕ НА СЖАТИЕ ОБРАЗЦОВ ИЗ ДРЕВЕСНОГО полимер-ПЕСЧАНОГО композита
TEST FOR COMPRESSION OF SAMPLES FROM WOOD POLYMER-THE SANDY COMPOSITE
Стородубцева Т. Н., д. т. н., профессор,
Давыдов Н., студент,
ФГБОУ ВПО «Воронежская государственная
лесотехническая академия»,
г. Воронеж, Россия
DOI: 10.12737/10204
Аннотация: ни для кого не секрет, что древесина — это материал, который активно применяется в строительстве, ведь он обладает отличными эксплуатационными характеристиками, а наряду с тем имеет действительно красивый внешний вид. Тем не менее, и у него есть одна особенность: при обработке древесины образуется большое число отходов и обрезков, особенно в том случае, если изделие имеет сложную форму или большие габариты. На протяжении последних нескольких десятков лет актуальным был вопрос о более эффективном использовании данного материала. Во многом именно это повлияло на развитие производства фанеры, а затем и древесных плит. Но XXI век стал эпохой композитных материалов: можно с уверенностью сказать, что с появлением ДПК произошла очередная промышленная революция. Любой материал характеризуется некоторыми параметрами. Одной из главных характеристик ДПК является предел прочности при сжатии. В статье приведена методика и результаты испытания древесного полимер-песчаного композита на сжатие.
Summary: for anybody not a secret that wood — is material which is actively applied in construction, after all it possesses excellent operational characteristics, and along with that has really beautiful appearance. Nevertheless, and it has one feature: when processing wood the large number of waste and scraps, especially is formed in case the product has a difficult form or big dimensions. For the last several tens years the question of more effective use of this material was actual. In many respects it influenced development of production of plywood, and then and wood plates. But the XXI century became an era of composite materials: it is possible to tell with confidence that with the advent of DPK there was the next industrial revolution. Any material is characterized by some parameters. One of the main characteristics of DPK is strength at compression. The technique and results of test wood polymer - a sand composite on compression is given in article.
Ключевые слова: древесина, композиционные материалы, испытания на сжатие
Keywords: wood , composite materials, compression tests
Вопрос о вторсырье в России является на сегодняшний день довольно важным и требующим большого внимания как со стороны изготовителей всевозможной продукции, так и со стороны их потребителей. Гораздо проще и дешевле переработать уже отслужившие свое всевозможные предметы и товары или отходы, образующиеся при их производстве, нежели закупать только недавно добытое сырье.