The results of studies on the synthesis of BN-Si3N4-Si composition in the SHS mode are presented. It was found that it was not possible to obtain Si3N4 in the product from the systems selected for the study. However, the final product consisted of a BN-Si composition, which is a powder with a nanometer particle size.
self-propagating high-temperature synthesis, nitride composition, sodium azide, precursor, powder.
1. Amosov A.P., Bichurov G.V. Azide technology of self-propagating high-temperature synthesis of micro- and nanopowders of nitrides: Monograph. M.:Mashinostroenie-1, 2007.- 526 p.
2. Bichurov G.V., Shiganova L.A., Titova Yu.V. Azide technology of self-propagating high-temperature synthesis of micro- and nanopowders of nitride compositions: Monograph.- M.: Mashinostroenie, 2012.- 519 p.
3. Bichurov G.V. The Use of Halides in SHS Azide Technology / International Journal of Self-Propagating High-Temperature Synthesis. 2000. Vol.9, No.2.- P. 247-268.
4. Kondratieva L.A. The use of the KBF4 halide salt in the preparation of the Si3N4-BN nitride composition / Scientific online publication «A POSTERIORI».- Moscow.- 2017.- pp.8-11.
5. Kondratieva L.A. Obtaining a Si3N4-BN nitride composition from the «KBF4+(NH4)2SiF6+NaN3» system using SHS-Az technology / International Scientific and practical Conference «Materials and methods of innovative research and development». Yekaterinburg, 2017. pp. 68-70.
6. Kondratieva L.A. Self-propagating high-temperature synthesis of powders of nitride compositions Si3N4-TiN, Si3N4-AlN, Si3N4-BN, AlN-BN, AlN-TiN, BN-TiN using sodium azide and halide salts: dissertation of the Doctor of technology.sciences. Samara: SamSTU.- 2018.- 881 p.